6063 Aluminyum Alaşımlarının Korozyon Direnci Üzerine Anadizasyon Öncesi Yüzey İşlemlerinin Ve Aa Anodizasyonla Üretilmiş İnce Oksit Filmlerinin Etkisi
6063 Aluminyum Alaşımlarının Korozyon Direnci Üzerine Anadizasyon Öncesi Yüzey İşlemlerinin Ve Aa Anodizasyonla Üretilmiş İnce Oksit Filmlerinin Etkisi
dc.contributor.advisor | Çakır, Ali Fuat | tr_TR |
dc.contributor.author | Sertçelik, Feriha | tr_TR |
dc.contributor.department | Malzeme | tr_TR |
dc.contributor.department | Materials | en_US |
dc.date | 1999 | tr_TR |
dc.date.accessioned | 2015-12-10T12:06:45Z | |
dc.date.available | 2015-12-10T12:06:45Z | |
dc.description | Tez (Doktora) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 1999 | tr_TR |
dc.description | Thesis (PhD) -- İstanbul Technical University, Institute of Science and Technology, 1999 | en_US |
dc.description.abstract | Bu çalışmada, 6063 aluminyum alaşımlarına uygulanan anodizasyon öncesi yüzey işlemlerinin, AA ve DA anodizasyonu ile sülfürik asit ve molibdat iyonu içeren sülfürik asit çözeltilerinde oluşturulmuş ince (4-5 mm) anodik oksit filmlerininin bu alaşımların korozyon özelliklerine etkileri incelenmiştir. Bu incelemelerde, temel olarak taramalı elektron mikroskobu (SEM), elektrokimyasal empedans spektroskopisi (EIS) ve bakır dekorasyonu teknikleri kullanılmıştır.Anodizasyon öncesi yüzey işlemlerinden kostik dağlama işlem süresi arttıkça yüzeylerin korozyon direnci düşerken nitrik asit çözeltisinde dağlama ürünlerininin temizlenmesi işlem süresinin artması ise yüzeylerin korozyon direncini arttırmıştır. Sülfürik asit AA filmler molibdatlı çözeltilerde elde edilen AA filmlerinden ve sülfürik asit DA filmlerinden de daha yüksek korozyon göstermiştir. Alaşımdaki metallerarası faz partiküllerinin hem anodizasyon öncesi yüzey işlemlerinden sonra hem de anodizasyondan sonra yüzeylerin korozyon direncinin azalmasında önemli bir rolü olduğu saptanmıştır. | tr_TR |
dc.description.abstract | In this study, the effect of pretreatment and thin (4-5 mm) anodic oxide films produced by AC and DC anodization in sulfuric acid and molybdate containing sulfuric acid on the corrosion properties of 6063 aluminium alloys was investigated. Scanning electron microscopy (SEM), electrochemical impedance spectroscopy and copper decoration technique were used for the investigation. Anodization pretreatments used in this study were caustic etching and desmutting in nitric acid solution. Increased caustic etching time caused decreased corrosion resistance of the surfaces while increased desmutting time increased corrosion resistance of the surfaces. Sulfuric acid AC anodized surfaces showed higher corrosion resistance than both sulfuric acid DA anodized and molybdate containing sulfuric acid AC anodized surfaces. It was determined that intermetallic particles and changes in their composition depending on surface pretreatment time on the surfaces played an important role on the decreased corrosion resistance of the both anodized and unanodized but pretreated surfaces. | en_US |
dc.description.degree | Doktora | tr_TR |
dc.description.degree | PhD | en_US |
dc.identifier.uri | http://hdl.handle.net/11527/11271 | |
dc.publisher | Fen Bilimleri Enstitüsü | tr_TR |
dc.publisher | Instıtute of Science and Technology | en_US |
dc.rights | İTÜ tezleri telif hakkı ile korunmaktadır. Bunlar, bu kaynak üzerinden herhangi bir amaçla görüntülenebilir, ancak yazılı izin alınmadan herhangi bir biçimde yeniden oluşturulması veya dağıtılması yasaklanmıştır. | tr_TR |
dc.rights | İTÜ theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. | en_US |
dc.subject | Korozyon | tr_TR |
dc.subject | 6063 aluminyum alaşımı | tr_TR |
dc.subject | yüzey işlemi | tr_TR |
dc.subject | empedans | tr_TR |
dc.subject | bakır dekorasyonu | tr_TR |
dc.subject | Corrosion | en_US |
dc.subject | 6063 aluminium alloy | en_US |
dc.subject | surface pretreatment | en_US |
dc.subject | impedance | en_US |
dc.subject | copper decoration | en_US |
dc.title | 6063 Aluminyum Alaşımlarının Korozyon Direnci Üzerine Anadizasyon Öncesi Yüzey İşlemlerinin Ve Aa Anodizasyonla Üretilmiş İnce Oksit Filmlerinin Etkisi | tr_TR |
dc.title.alternative | The Effect Of Pretreatment And Thin Layer Sulfuric Acid Ac Anodization Of 6063 Aluminum Alloys On Its Corrosion Resistance | en_US |
dc.type | Doctoral Thesis | en_US |