Ağırlıkça % 2 Mgo Ve Tio2 Katkılı Alümina Seramiğinin Farklı Sıcaklıklarda Sinterlenmesi Ve Karakterizasyonu

dc.contributor.advisor Addemir, Abdülkadir Okan tr_TR
dc.contributor.author Çinaz, Ender tr_TR
dc.contributor.authorID 424663 tr_TR
dc.contributor.department Malzeme Mühendisliği YL. tr_TR
dc.contributor.department Materials Engineering MSc. en_US
dc.date 2012 tr_TR
dc.date.accessioned 2012-02-26 tr_TR
dc.date.accessioned 2015-09-17T12:48:03Z
dc.date.available 2015-09-17T12:48:03Z
dc.date.issued 2012-02-29 tr_TR
dc.description Tez (Yüksek Lisans) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2012 tr_TR
dc.description Thesis (M.Sc.) -- İstanbul Technical University, Institute of Science and Technology, 2012 en_US
dc.description.abstract Yüksek aşınma direnci, kimyasal kararlılığı, yüksek sıcaklıklara karşı dayanıklı olması, yüksek elastik modülü ve düşük maliyetli tozları ile alümina günümüzde seramik malzemeler arasında önemli bir yere sahiptir. Geleneksel yöntemler kullanılduğında istenen yoğunlukta alumina üretmek için 1700°C’nin üzerinde sıcaklıklar gerekir. Yüksek sıcaklıklarda sinterleme hem ekonomik değildir hemde üretim zorluklarını beraberinde getirir. Bu nedenle aluminanın düşük sıcaklıklarda sinterlenmesi için bazı katkıların kullanılması gerekmektedir. Bu katkılar genellikle; Cr2O3, MgO, TiO2, MnO2, MnO ve ZrO2’dir. Bu çalışmada amaç ağırlıkça %2 MgO ve %2 TiO2 katkısıyla alüminanın düşük sıcaklıklarda ve istenen özelliklerde sinterlenebilmesini sağlamaktır. Ağırlıkça %2 MgO ve %2 TiO2 katkılı alümina elde etmek için öncelikle toz karışımları hazırlanmış, bağlayıcı ve ethanol katksıyla atritörde karıştırılarak homojen bir karışım sağlanmıştır. Etüvde kurutularak ethanol katkısı uzaklaştırılan karışım soğuk preslemede 200 MPa yük altında şekillendirilmiştir. Bağlayıcı uçurma fırınında kurutulan numuneler 1300°C, 1400°C ve 1500°C’de 2 saat sinterlenmiştir. Sinterlenen numunelerin özelliklerinin belirlenmesi amacıyla pişme küçülmesi, yoğunluk, üç nokta eğme mukavemeti ve sertlik deneyleri yapılmıştır. Ayrıca XRD ile sinterleme sonrası oluşabilecek fazlar belirlenmiş, SEM ile de başlangıç tozları ve sinterlenen malzemelerin mikroyapı incelemeleri yapılmıştır. Yapılan bu fiziksel ve mekanik testler neticesinde üretilen MgO ve TiO2 katkılı alümina seramik malzemenin özellikleri üzerine sinterleme sıcaklığının etkileri incelenmiş, sonuçlar verilmiş ve tartışılmıştır. Ağırlıkça %2 MgO ve %2 TiO2 katkılı alüminanın 1300 ve 1400°C’de sinterlenmesi sonucu malzemede yüksek porozite ve düşük yoğunluk özellikleri nedeniyle istenen sonuç sağlanamamıştır. Ancak 1500°C sinterleme sıcaklığında olumlu sonuçlar alınmıştır ve alüminanın katkılarla nispeten düşük sıcaklıklarda sinterlenebileceğini göstermiştir tr_TR
dc.description.abstract Alumina is one of the important ceramic materials due to its high wear resistance, high chemical resistance, high temperature stability and low cost starting powder. If alumina powders are prepared by tradiotional methods, the sintering temperature should be over 1700°C to get a dense alumina sintered body. Sintering at high temperatures is not economic and has some difficulties at production. For sintering at low temperatures some additives must be added to the composition of alumina. The main aim of this study is to sinter 2 wt. % MnO and 2 wt. % TiO2 added alumina at lower sintering temperatures. Firstly, powder compositions are wet milled with ceramic binder and ethanol to obtain a homogeneous mixture and then dried in drying oven. And powder mixture were pressed. Pressed and dried specimens were sintered for 2 hours at 1300°C, 1400°C and 1500°C. To investigate of the sintered specimens properties firing shrinkage, density, three point bending strength and hardness tests were done. Furthermore, phases formed after sintering were detected by XRD analysis. Microstructural analysis of initial powders and sintered specimens were characterized by SEM. With the assistance of physical and mechanical experiments results, the effect of sintering temperature on the sintered samples properties are given and discussed. Results of sintering 2 wt. % MgO and 2 wt. % TiO2 added alumina at 1300 and 1400°C was not successful because of high porosity and lower density. But also good results of sintering at 1500°C showed that alumina can be sintered at lower sintering temperature. en_US
dc.description.degree Yüksek Lisans tr_TR
dc.description.degree M.Sc. en_US
dc.identifier.uri http://hdl.handle.net/11527/9460
dc.publisher Fen Bilimleri Enstitüsü tr_TR
dc.publisher Institute of Science and Technology en_US
dc.rights İTÜ tezleri telif hakkı ile korunmaktadır. Bunlar, bu kaynak üzerinden herhangi bir amaçla görüntülenebilir, ancak yazılı izin alınmadan herhangi bir biçimde yeniden oluşturulması veya dağıtılması yasaklanmıştır. tr_TR
dc.rights İTÜ theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. en_US
dc.subject sinterleme tr_TR
dc.subject karakterizasyon tr_TR
dc.subject alümina tr_TR
dc.subject seramik tr_TR
dc.subject sintering en_US
dc.subject characterization en_US
dc.subject alumina en_US
dc.subject ceramic en_US
dc.title Ağırlıkça % 2 Mgo Ve Tio2 Katkılı Alümina Seramiğinin Farklı Sıcaklıklarda Sinterlenmesi Ve Karakterizasyonu tr_TR
dc.title.alternative Sintering Of 2 Wt. % Mgo And 2 Wt. % Tio2 Doped Alumina Ceramic At Different Temperatures And Its Characterization en_US
dc.type Thesis en_US
dc.type Tez tr_TR
Dosyalar
Orijinal seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.placeholder
Ad:
12416.pdf
Boyut:
2.07 MB
Format:
Adobe Portable Document Format
Açıklama
Lisanslı seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.placeholder
Ad:
license.txt
Boyut:
3.14 KB
Format:
Plain Text
Açıklama