Toz Metalurjisi Yöntemiyle Alüminyum Matrisli Bor Karbür Takviyeli Kompozitlerin Üretilmesi Ve Mekanik Özelliklerinin İncelenmesi
Toz Metalurjisi Yöntemiyle Alüminyum Matrisli Bor Karbür Takviyeli Kompozitlerin Üretilmesi Ve Mekanik Özelliklerinin İncelenmesi
dc.contributor.advisor | Kayalı, Eyüp Sabri | tr_TR |
dc.contributor.author | Akın, Gürkan | tr_TR |
dc.contributor.department | Malzeme Bilimi ve Mühendisliği | tr_TR |
dc.contributor.department | Material Science and Engineering | en_US |
dc.date | 2006 | tr_TR |
dc.date.accessioned | 2015-10-06T13:43:12Z | |
dc.date.available | 2015-10-06T13:43:12Z | |
dc.description | Tez (Yüksek Lisans) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2006 | tr_TR |
dc.description | Thesis (M.Sc.) -- İstanbul Technical University, Institute of Science and Technology, 2006 | en_US |
dc.description.abstract | Bu çalışmada, toz metalurjisi yöntemi kullanılarak matrisi %100 Al ve %50 Al-%50 Al12Si olan, ağırlıkça %4-%23 oranında bor karbür (B4C) partikül takviyesi yapılmış kompozitlerin optimum üretim parametreleri, aşınma ve korozyon davranışları incelenmiştir. Kompozitlerin üretimine ait optimum koşullara, metalik tozların 8 tonluk yük altında preslenmesi ve 570 °C’de atmosferik ortamda 12 saat süreyle sinterlenmesi sonucunda ulaşılmıştır. Artan B4C miktarı ve matrise yapılan Al12Si ilavesiyle kompozitlerin sertliği artış göstermektedir. En yüksek aşınma direncine ise matrisi %50 Al–%50Al12Si olan ve %9 B4C takviyesi yapılmış kompozitlerde ulaşılmıştır. Kompozitlerdeki B4C içeriğinin %9’un üzerine çıkarılması sertliği artırmasına karşın aşınma direncinde azalmaya neden olmuştur. Bu kompozitlere ara işlem olarak oda sıcaklığında basma yönünde uygulanan %20 oranındaki deformasyon, aşınma direncinde ilave bir artış sağlamıştır. Korozyon deneyleri, matrisi %100 Al olan ve B4C takviyesi içermeyen malzemede korozyon kaybının en az olduğu sonucunu vermiştir. | tr_TR |
dc.description.abstract | In this study, optimum production parameters, wear and corrosion behaviour of composites having 100% Al and 50% Al-50% Al12Si matrix and reinforced with boron carbide (4% to 23% by weight) were investigated using powder metallurgy method. Optimum production conditions of composites were obtained by compacting powders under a load of 8 tons and performing atmospheric sintering at 570 °C during 12 hours. Increasing of B4C content and Al12Si addition into the matrix caused an increase at the hardness of the composites. Highest wear resistance was obtained at 9% B4C reinforced 50%Al-50% Al12Si matrix composite. Up to 9% B4C content, wear resistance of composites increased however it decreased with further increase of B4C content. Additionally, performing 20% compressive deformation at room temperature also increased the hardness of the composites. In corrosion tests, minimum corrosion loss was occured at the unreinforced aluminium matrix composite. | en_US |
dc.description.degree | Yüksek Lisans | tr_TR |
dc.description.degree | M.Sc. | en_US |
dc.identifier.uri | http://hdl.handle.net/11527/9599 | |
dc.publisher | Fen Bilimleri Enstitüsü | tr_TR |
dc.publisher | Institute of Science and Technology | en_US |
dc.rights | İTÜ tezleri telif hakkı ile korunmaktadır. Bunlar, bu kaynak üzerinden herhangi bir amaçla görüntülenebilir, ancak herhangi bir biçimde yeniden oluşturulması veya dağıtılması yazılı izin alınmadan yasaklanmıştır. | tr_TR |
dc.rights | İTÜ theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. | en_US |
dc.subject | toz Metalurjisi | tr_TR |
dc.subject | alüminyum | tr_TR |
dc.subject | bor karbür (B4C) | tr_TR |
dc.subject | powder metallurgy | en_US |
dc.subject | aluminium | en_US |
dc.subject | boron carbide (B4C) | en_US |
dc.title | Toz Metalurjisi Yöntemiyle Alüminyum Matrisli Bor Karbür Takviyeli Kompozitlerin Üretilmesi Ve Mekanik Özelliklerinin İncelenmesi | tr_TR |
dc.title.alternative | Production Of Boron Carbide Reinforced Aluminium Matrix Composites Using Powder Metallurgy Method And Investigation Of Their Mechanical Properties | en_US |
dc.type | Master Thesis | en_US |