Kompozit Panel Yapı Malzemelerinin Mekanik Özelliklerinin Araştırılması

dc.contributor.advisor Pekmezci, Bekir Yılmaz tr_TR
dc.contributor.author Arabacı, Egemen tr_TR
dc.contributor.authorID 10064434 tr_TR
dc.contributor.department İnşaat Mühendisliği tr_TR
dc.contributor.department Civil Engineering en_US
dc.date 2015 tr_TR
dc.date.accessioned 2017-03-10T08:40:28Z
dc.date.available 2017-03-10T08:40:28Z
dc.date.issued 2015-02-05 tr_TR
dc.description Tez (Yüksek Lisans) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2015 tr_TR
dc.description Thesis (M.Sc.) -- İstanbul Technical University, Instıtute of Science and Technology, 2015 en_US
dc.description.abstract Son yıllarda kompozit panel malzemeler yapının diğer bileşenleri ile olan uyumu, kolay uygulanabilirliği ve temin edilebilirliği avantajları sayesinde inşaat sektöründe ilgi görmekte ve sıkça tercih edilmektedir.  Bu çalışma kapsamında, yapıların iç ve dış mekanlarında sıkça uygulanan kompozit panel malzemelerinin mekanik özelliklerinin araştırılması ve elde edilen sonuçlara göre daha üstün özelliklere sahip kompozit panel malzemesi üretilmesi amaçlanmıştır. Bu amaçla çimento esaslı kesik cam lifli, sürekli cam lifli ve lifsiz olmak üzere üç çeşit üretim su/çimento oranı sabit tutularak yapılmıştır. Cam lifli üretimler ağırlıkça %1,5 ve %2,5 cam lif kullanılarak gerçekleştirilmiştir. Çalışma kapsamında, endüstriyel olarak üretilen ve sektörde kabul görmüş, yaygın olarak kullanılan kompozit panel malzemeler ile bu kapsamda üretimi gerçekleştirilen malzemeler üzerinde eğilme, çekme,  su emme ve genleşme oranı tayini deneyleri yapılmıştır.  Kompozit panellere yapılan dört noktalı eğilme deneyi neticesinde ilk olarak üretimi gerçekleştirilen numuneler karşılaştırılmıştır. Bu doğrultuda lif oranının artmasıyla beraber kesik cam lif donatılı numunelerde eğilme dayanımının arttığı gözlemlenmiştir. Aynı şekilde kesik cam lif oranın artmasıyla beraber kırılma enerjisinin de arttığı görülmüştür. Sürekli cam lif donatılı üretimlerin eğilme dayanımları karşılaştırıldığında lif artışıyla beraber eğilme dayanımında önemli bir artış olmadığı gözlemlenmiştir. Bunun nedeninin liflerin matris ile yeterli aderansı sağlayamadığından kaynaklandığı düşünülmektedir.  Endüstriyel olarak üretilen ve sektörde kabul görmüş panel malzemelerine yapılan dört noktalı eğilme deneyi sonucunda selülozik lif içeren çimento esaslı paneller en yüksek eğilme dayanımı sonucunu verirken, gevrek bir davranış göstererek ani göçme yaptığı belirlenmiştir. Tekstil donatılı çimento esaslı panel malzemesinin kullanılan lif tipinin bir düzlemde sürekli olması ve donatının matris ile aderansının yüksek olmasından dolayı en yüksek enerji yutma kapasitesine sahip olduğu görülmüştür, ancak eğilme dayanımı diğer panellerin altında kalmıştır.  Kompozit panellere yapılan çekme deneyi sonucunda tekstil donatıya sahip çimento esaslı panelin çoklu çatlaklar oluşturarak ani kopma yapmadığı gözlemlenmiştir. Selülozik lifli çimento esaslı panellerin en yüksek çekme dayanımına sahip olduğu belirlenirken deformasyon miktarının diğer panellerin altında kaldığı görülmüştür. Sürekli cam lifli kompozitlerde ağırlıkça lif oranın artmasının kompozitin deformasyon miktarını arttırıcı yönde etkilediği görülürken çekme dayanımının artmasına etkisi olmadığı sonucu elde edilmiştir. Kesikli cam lifli kompozitlerde lif oranın artmasıyla deformasyon miktarının arttığı belirlenmiştir. Panel malzemelerde yapılan su emme deneyi sonucunda magnezyum oksit esaslı kompozitin en yüksek su emme oranına sahip olduğu görülmüştür.  Selüloz ve  ahşap lif içeren panel malzemelerin su emme oranlarının çimento esaslı tekstil donatılı panele oranla çok daha yüksek olduğu tespit edilmiştir. Bunun nedeninin selülozik ve ahşap liflerin su emme kapasitelerinin yüksek olmasından kaynaklandığı düşünülmektedir. Üretimi gerçekleştirilen çimento esaslı cam lif donatılı numuneler üzerinde yapılan su emme deneyleri sonucunda su emme değerlerinin birbirlerine yakın ve diğer panel malzemelerine göre su emmesinin çok az olduğu belirlenmiştir. Genleşme oranı tayini deneyi sonuçlarına göre en yüksek su emme değerine sahip olan magnezyum oksit esaslı kompozitin en yüksek genleşme oranına sahip olduğu belirlenmiştir. Çalışma kapsamında üretimi gerçekleştirilen çimento esaslı cam lif donatılı numunelerin daha düşük genleşme oranına sahip olduğu görülmüştür. Bu sonucun üretilen cam lif donatılı kompozit panellerin düşük su emme oranına sahip olmasından kaynaklandığı söylenebilir.  Eğilme dayanımları, kırılma enerjileri, su emme ve genleşme oranı tayini deneyi sonuçları bir bütün olarak ele alındığında çalışma kapsamında üretimi gerçekleştirilen ağırlıkça %2,5 kesik cam lif içeren çimento esaslı kompozitlerin, eğilme dayanımını yüksek, yük etkisi altında sünek davranış gösteren, düşük su emme ve genleşme oranlarına sahip bir kompozit olduğu sonucuna varılmıştır. tr_TR
dc.description.abstract Composite panels are widely used and preferred in the recent years due to their benefits such as compatibility with different structures, practicability, and easily findability in the field of civil engineering.   In the scope of this thesis, composite panels are analyzed for its mechanical properties due to its applicability to both interior and exterior places. The aim of the thesis is the production of high performance composite panels depending on the result of the experiments that conducted during the study. Composite panels are produced by holding the same water/cement ratio based on three types such as cement based batch glass fiber, continuous glass fiber and non-glass fiber. The production of cement based glass fiber consist of 1,5 % and 2,5 % glass fiber percentage by weight. In this study, composite panels that are widely used in the civil engineering field and the produced materials are subjected to bending, tension, water absorbtion, expansion ratio experiments.   As a result of a four-point bending test on commercially accepted panel materials, it is observed that cement-based cellulosic fibers have high-fold strength while taking a sudden intrusion behavior. Textile combined cement-based panel materials have high energy ingest capacity due to continuous usage of fiber, the same platform and higher adhesion between matrix and reinforcement. Its bending strength is lower than other panels.  In the thesis of samples being produced industrially in the sector of water absorption and expansion ratio accepted by a panel production has been shown to have a lower value. The amount of fibers, the effect of water absorption and rate of expansion was observed. As a result of the tensile test performed on the panel cement-based composite panel with textile reinforcement has been observed to sudden rupture creating multiple cracks.  Cellulosic fibrous cements based panel that has the highest tensile strength in determining the amount of deformation was found to be under the other panel. Cement-based cellulosic fiber panels exhibit a brittle fracture behavior without multiple cracks despite the high flexural strength. Depending on the low deformation capacity of the panels has a low refractive power. Textile-reinforced cementitious composite panels, by forming multiple cracks under impact load through the textile reinforcement used and shows behavior by highly ductile deformation. Therefore, these panels have a high fracture energy. The result that the continuous glass fiber composite fiber percentage increase in weight was observed that the amount of tensile deformation of the composite in the direction of increasing its effect is to increase strength effects were obtained. Discrete glass fiber composite is determined that the amount of deformation increases with increasing the amount of fiber. Industrial production as performed in the sector panel accepted dissertation samples and scope of production elasticity modulus of the panel according to the results of the tensile tests conducted on mixtures performed were calculated. According to the obtained results, it was found that reduction of the production is performed in discrete glass fiber mixture ratio increases the elasticity modulus. The mixture held with continuous production of glass fiber could not be determined in a systematic behavior.  Industrially panel production elasticity modulus textile reinforced cementitious has been determined that there is a high deformation under a very low load case of the panel according to the other panel. Tensile strength is the highest cellulose based fiber cement panels are panels with the highest modulus of elasticity. Modulus of elasticity of cement-based wood chip panel and magnesium oxide based textile-reinforced panel sample average has increased compared to the other panel. Discrete glass fiber-reinforced cement produced under experimental work based on the results obtained from tests on composites; increasing the amount of glass fiber increases, the bending strength increased by the amount of deformation after break, fracture energy increases. Continuous glass fiber reinforced concrete, in order to fully realize the matrix fibers penetration, a systematic increase in strength with the amount of fibers could not be detected. Water absorption is conducted on panel materials and magnesium oxide based composite panel was found to have the highest water absorption ratio. The water absorption capacity of cellulose and wood fiber panels are higher than textile reinforced cementitious panels. It is noted that the result of high ratio of cellulose and wood fibers depending on its high water absorption capacity. The water absorption capacity values are closed to each other of produced cement based glass fiber samples and their water absorption level is low compared to other panel material’s level. As a result of expansion contraction analysis magnesium oxide based composite panel which has high water absorption capacity has also the highest contraction ratio although produced cement based glass fiber materials has the smallest expansion contraction ratio. It is noted that due to the low water absorption ratio, the produced glass fiber composite panel has the smallest contraction ratio.  During the assessment of the result of bending strength, fracture energy, water absorption and expansion shrinkage analysis as a whole, in the scope of the thesis, production of cement-based composites containing held by weight 2,5% glass fiber has high bending strength, showing ductile behavior under load impact, low water absorption.  This work process based on experimental results and observations obtained in studies subsequent high energy absorption capacity and flexural strength to be used in combination to achieve optimum continuous and chopped glass fibers in the body. Subsequent studies, penetration problems occurring in continuous fibers must be taken into account. en_US
dc.description.degree Yüksek Lisans tr_TR
dc.description.degree M.Sc. en_US
dc.identifier.uri http://hdl.handle.net/11527/13878
dc.publisher Fen Bilimleri Enstitüsü tr_TR
dc.publisher Institute of Science and Technology en_US
dc.rights İTÜ tezleri telif hakkı ile korunmaktadır. Bunlar, bu kaynak üzerinden herhangi bir amaçla görüntülenebilir, ancak yazılı izin alınmadan herhangi bir biçimde yeniden oluşturulması veya dağıtılması yasaklanmıştır. tr_TR
dc.rights İTÜ theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. en_US
dc.subject Çimento Esaslı Kompozit Paneller tr_TR
dc.subject Cement Based Composite Panels en_US
dc.title Kompozit Panel Yapı Malzemelerinin Mekanik Özelliklerinin Araştırılması tr_TR
dc.title.alternative Investigation On The Mechanical Properties Of Composites Panel Materials en_US
dc.type Thesis en_US
dc.type Tez tr_TR
Dosyalar
Orijinal seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.alt
Ad:
10064434.pdf
Boyut:
9.55 MB
Format:
Adobe Portable Document Format
Açıklama
Lisanslı seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.placeholder
Ad:
license.txt
Boyut:
3.16 KB
Format:
Plain Text
Açıklama