Electrocatalytic performance of interconnected self-standing tin nanowire network produced by AAO template method for electrochemical CO2 reduction

(Wiley, 2023) Er, Dilan ; Avcı, Burçak ; Ürgen, Mustafa ; orcid.org/0009-0008-2120-2994 ; orcid.org/0000-0003-3549-0049 ; Metalurji ve Malzeme Mühendisliği

In this study, we used a specially designed aluminum anodic oxide (AAO) template technique to produce interconnected self-standing tin nanowire electrocatalysts having a high surface-to-volume ratio for CO2 reduction toward formate. These electrodes consisted of interconnected tin nanowires with 150 nm diameter and 7 μm length supported on 70–100 μm thick tin film. As prepared electrodes produced 6 times higher formate than the flat tin sheets, yet Faradaic efficiencies (FE%) were unsatisfactory. The main reason for low FE% is determined as the etching of native oxide on tin nanowires during hot alkali treatment to remove AAO and remnant aluminum. Porous anodic oxidation in 1 M NaOH solution was realized to recover tin oxides on the surface. Anodized tin nanowire electrocatalysts produced higher formate than anodized tin sheets, reaching FEformate% of ~87 at −1 V vs. RHE cathodic reduction potential. Moreover, while anodic oxide on flat tin flaked off the surface in 1 h, these electrodes preserved their integrity and formate production ability even after 12 h.