Alüminyum Sürekli Döküm Yöntemi İle Üretilmiş 5052 – 5182 Alüminyum Alaşımlarının Şekillendirilebilirlik Kabiliyetlerinin Belirlenmesi

dc.contributor.advisor Kayalı, E. Sabri tr_TR
dc.contributor.author Alper, M.gökhan tr_TR
dc.contributor.department Malzeme tr_TR
dc.contributor.department Materials en_US
dc.date 2003 tr_TR
dc.date.accessioned 2015-09-11T11:16:41Z
dc.date.available 2015-09-11T11:16:41Z
dc.description Tez (Yüksek Lisans) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2003 tr_TR
dc.description Thesis (M.Sc.) -- İstanbul Technical University, Institute of Science and Technology, 2003 en_US
dc.description.abstract Bu çalışmada, Twin-Roll Casting metoduyla 5 mm kalınlığında dökülmüş ve 1 mm kalınlığa soğuk haddelenerek endüstriyel ortamda tavlanmış yüksek magnezyumlu iki alüminyum alaşımının (5052-5182) şekillenme kabiliyetleri yapılan çeşitli mekanik deneylerle çizilen şekillendirme sınır diyagramları yardımıyla deneysel çalışmalar yardımı ile incelenmiştir. Yapılan deneysel çalışmalarda, 5182 (%4,4 Mg) alaşımının, 5052 (%2,6 Mg) alaşımına göre daha yüksek mukavemet, Erichsen, dikey anizotropi ve deormasyon sertleşmesi üssü (n) değerlerine sahip olduğu saptanmıştır. Düzlemsel anizotropi katsayıları karşılaştırıldığında iki alaşım arasında belirgin bir farkın olmadığı tespit edilmiştir. Yapılan çekme deneylerinde, her iki alaşımda da plastik deformasyon sırasında dinamik deformasyon yaşlanması görülmüştür. Döküm mikroyapıları incelendiğinde, her iki yapıda da merkez hattı segregasyonuna rastlanmıştır. Homojen tavlanan numunelerin kesitlerinde dış yüzeylerde ince tane yapısı, iç bölgelere doğru daha kaba tane yapısına rastlanmıştır. Her iki alaşımın nihai kalınlıkta çekme numuneleri kırılma yüzeyleri taramalı elektron mikroskobunda incelendiğinde, sünek kırılmayı temsil eden oyuklu kırılma yüzeylerine rastlanmıştır. Hidrolik şişirme ve çentik çekme testleri ile oluşturulan Şekillendirme Sınır Diyagramlarından, 5182 alaşımının 5052 alaşımına göre daha iyi şekillendirilebilirlik gösterdiği tespit edilmiştir tr_TR
dc.description.abstract In this study, the formability behaviours of two 5xxx quality aluminium alloys (5052 and 5182) which cast by twin roll casting method in approximately 5 mm thickness then cold rolled to 1 mm and finally annealed condition were investigated. From the mechanical test results, it was determined that 5182 quality aluminium alloy has higher strength, Erichsen, normal anisotrophy and strain hardening exponent (n) values than 5052 quality aluminium alloy. From the planar anisotrophy values, it was also determined that 5052 quality aluminium alloy has approximately no earing behaviour, whereas 5182 aluminium alloy has earing behaviour at the direction of 450. At the tensile tests of the both aluminium alloys the dynamic strain aging behaviour was observed. The ductility values of these two alloys were close each other. At the metallographic examinations, it was observed that these two aluminium alloys have center-line segregation. At the same time, after homogenisation of cast microstructures, the grain structures changed from surface as fine grains toward to center as coarse grains. Scanning electron microscope examinations of the fracture surfaces of the tensile specimens of both alloys showed ductile fracture characteristics such as dimpled fracture surfaces. Forming limit diagrams of these two aluminium alloys were obtained from hydraulic bulge and notched tensile tests to compare formability behaviours. It is found that 5182 aluminium alloy has better formability than 5052 aluminium alloy. en_US
dc.description.degree Yüksek Lisans tr_TR
dc.description.degree M.Sc. en_US
dc.identifier.uri http://hdl.handle.net/11527/9326
dc.publisher Fen Bilimleri Enstitüsü tr_TR
dc.publisher Institute of Science and Technology en_US
dc.rights İTÜ tezleri telif hakkı ile korunmaktadır. Bunlar, bu kaynak üzerinden herhangi bir amaçla görüntülenebilir, ancak yazılı izin alınmadan herhangi bir biçimde yeniden oluşturulması veya dağıtılması yasaklanmıştır. tr_TR
dc.rights İTÜ theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. en_US
dc.subject Şekillendirme Sınır Diyagramları tr_TR
dc.subject ikiz merdane dökümü tr_TR
dc.subject 5xxx alüminyum alaşımları tr_TR
dc.subject Forming Limit Diagram en_US
dc.subject Twin-Roll Casting en_US
dc.subject 5xxx aluminium alloys en_US
dc.title Alüminyum Sürekli Döküm Yöntemi İle Üretilmiş 5052 – 5182 Alüminyum Alaşımlarının Şekillendirilebilirlik Kabiliyetlerinin Belirlenmesi tr_TR
dc.title.alternative Determination Of Formability Behaviours Of 5052 And 5182 Aluminium Alloys Produced By Continuous Casting Method en_US
dc.type Thesis en_US
dc.type Tez tr_TR
Dosyalar
Orijinal seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.alt
Ad:
1495.pdf
Boyut:
6.6 MB
Format:
Adobe Portable Document Format
Açıklama
Lisanslı seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.placeholder
Ad:
license.txt
Boyut:
3.14 KB
Format:
Plain Text
Açıklama