Atık Akü Pastalarından Elektrolitik Olarak Kurşun Geri Kazanımı

dc.contributor.advisor Timur, Servet tr_TR
dc.contributor.author Yolcu, Bengisu Müge tr_TR
dc.contributor.authorID 10005879 tr_TR
dc.contributor.department Üretim Metalurjisi tr_TR
dc.contributor.department Manufacturing en_US
dc.date 2013 tr_TR
dc.date.accessioned 2013-07-04 tr_TR
dc.date.accessioned 2015-09-07T07:56:34Z
dc.date.available 2015-09-07T07:56:34Z
dc.date.issued 2013-07-19 tr_TR
dc.description Tez (Yüksek Lisans) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2013 tr_TR
dc.description Thesis (M.Sc.) -- İstanbul Technical University, Institute of Science and Technology, 2013 en_US
dc.description.abstract Bu çalışmada, mevcut kurşun-asit akü geri dönüşüm proseslerine alternatif bir çözüm aranarak sıfır atık prensipli bir proses oluşturulmuştur. Bu proses kapsamında akü pastası içerisinde bulunan sülfat içeriği elektrolitik olarak giderilmiş ve elektrodiyaliz prensibi kullanılarak elektrolitik asit geri kazanımı gerçekleştirilmiştir. Ardından çalışmanın pirometalurjik kademesi olan ikinci aşamada, sülfatı giderilmiş pastadan düşük sıcaklıkta karbotermik redüksiyon ile metalik kurşun kazanılmıştır. Yapılan deneylerde 250 A/m2 akım yoğunluğu, 2,5 cm anot-katot mesafesi, oda sıcaklığı, 0,5 M H2SO4 konsantrasyonu şartlarında 8 saat süreyle elektroliz işlemi uygulandığında pastada başlangıçta %50 civarında olan PbSO4 içeriğinin %1’in altına düşürülebildiği görülmüştür. Elektrolitik asit geri kazanımı deneyleri sırasında anyonik membran ile ayrılmış iki bölmeli bir hücre tasarlanarak 24 saat süreyle elektroliz işlemi uygulanmış ve başlangıç asit konsantrasyonunun %50’den fazlası geri kazanılmıştır. Pirometalurjik aşamada yapılan çalışmalarda ise öncelikle kurşun bileşiklerinin uçuculuğu göz önüne alınarak düşük sıcaklıkta ergiyen örtücü flaks bileşimi (%70 NaCl+%30 KCl+%2 CaF2 – 1:2 Boraks:tuz) oluşturulmuştur. Örtücü flaks bileşimi altında yapılan deneylerde kurşun kaybı %1’in altına indirilmiştir. Flaks kalınlığının kurşun kaybına etkisi incelendiğinde 1 cm kalınlıkta flaks tabakasının yeterli örtücülüğü sağladığı görülmüştür. Karbotermik redüksiyon için uygun şartlar taranmış ve 800ºC’de, ağ. %7 karbon ile 1 saat süreyle yapılan deneylerde %93 verimle kurşun kazanımı gerçekleştirilmiştir. tr_TR
dc.description.abstract In this study, an alternative process to current lead-acid battery recycling processes has been developed. Within the process developed, sulphate content of battery paste is removed with electrolysis and waste battery electrolyte is regenerated. In the next step defined as the pyrometallurgical part of the process, desulphurised paste is reduced. Experimental work showed that PbSO4 content (%wt. 50 of the paste) can be reduced below %1, as a result of 8 hours of electrolysis (250 A/m2 current density, 2,5 cm anode-cathode distance, room temperature, 0,5 M H2SO4 concentration). Due to electrolytic acid regeneration experiments, two compartment cell divided by an anion exchange membrane, was designed and at the end of 24 hours of electrolysis over %50 of waste electrolyte was regenerated. For pyrometallurgical experiments, covering flux composition (%70 NaCl+%30 KCl+%2 CaF2 – 1:2 Borax:salt) was developed due to high volatility of lead compounds. As a result, metal loss was reduced below %1, by melting paste under covering flux. It was obtained that 1 cm of flux height can cover the melt efficiently. Optimum conditions for carbothermic reduction were examined and desulphurised paste was reduced with %93 efficiency under conditions of 800ºC, wt. %7 carbon, 1 hour of reduction time. en_US
dc.description.degree Yüksek Lisans tr_TR
dc.description.degree M.Sc. en_US
dc.identifier.uri http://hdl.handle.net/11527/9085
dc.publisher Fen Bilimleri Enstitüsü tr_TR
dc.publisher Institute of Science and Technology en_US
dc.rights İTÜ tezleri telif hakkı ile korunmaktadır. Bunlar, bu kaynak üzerinden herhangi bir amaçla görüntülenebilir, ancak yazılı izin alınmadan herhangi bir biçimde yeniden oluşturulması veya dağıtılması yasaklanmıştır. tr_TR
dc.rights İTÜ theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. en_US
dc.subject Kurşun-asit aküler tr_TR
dc.subject Elektroliz tr_TR
dc.subject Kurşun geri kazanımı tr_TR
dc.subject Lead-acid batteries en_US
dc.subject Electrolysis en_US
dc.subject Lead recycling en_US
dc.title Atık Akü Pastalarından Elektrolitik Olarak Kurşun Geri Kazanımı tr_TR
dc.title.alternative Electrolytic Lead Recycling For Waste Lead-acid Batteries en_US
dc.type Master Thesis en_US
Dosyalar
Orijinal seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.alt
Ad:
13781.pdf
Boyut:
2.56 MB
Format:
Adobe Portable Document Format
Açıklama
Lisanslı seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.placeholder
Ad:
license.txt
Boyut:
3.14 KB
Format:
Plain Text
Açıklama