Tabakalı Kompozit Plakaların Yarı Statik Penetrasyon Yükleri Altındaki Davranışlarının Araştırılması

Abstract

In this study, the behavior of carbon and S-glass fiber reinforced composite laminates under the quasi-static penetration loads was investigated, and compared with each other. Load to deformation according to punch shear ratios (SPR=Ds/Dp) was also examined. In this way, it was obtained the information about the energy absorption capacity of the composite laminates and variation of impact behaviors in terms of different punch ratios. Results showed that carbon/epoxy composite laminates exhibited better energy absorption capacity than S-glass/epoxy composite laminates. In addition, as the SPR ratio increases, the maximum force decreases, but the energy absorption capacity increases.Bu çalışmada, karbon ve S-cam fiber takviyeli tabakalı kompozit plakaların yarı statik penetrasyon yükleri altındaki davranışları incelenmiş ve karşılaştırılmıştır. Yüke karşı deformasyon özellikleri farklı kesme delme oranlarına (Ds/Dp) göre ele alınmıştır. Böylece kompozit plakaların enerji emme kapasiteleri hakkında ve hangi malzemenin hangi delme oranı altında daha iyi darbe davranışına sahip olacağı hakkında bilgi elde edilmiştir. Elde edilen sonuçlara göre, karbon/epoksi kompozit plakaların S-cam /epoksi plakalardan daha iyi enerji emme kapasitelerinin olduğunu ve (Ds/Dp) oranının artmasının maksimum kuvveti düşürdüğü, fakat enerji emme kapasitesini artırdığını göstermiştir.Conference Paper -- Theoretical and Applied Mechanical Turkish National Committee, 2015Konferans Bildirisi -- Teorik ve Uygulamalı Mekanik Türk Milli Komitesi, 2015