Al2o3 – Zro2 – Ceo2 Kompozitlerinin Spark Plazma Sinterleme (sps)yöntemi İle Üretimi Ve Karakterizasyonu

dc.contributor.advisor Göller, Gültekin tr_TR
dc.contributor.author Bilgiç, Betül Zeynep tr_TR
dc.contributor.authorID 432260 tr_TR
dc.contributor.department Malzeme tr_TR
dc.contributor.department Materials en_US
dc.date 2012 tr_TR
dc.date.accessioned 2012-07-03 tr_TR
dc.date.accessioned 2015-09-11T11:16:20Z
dc.date.available 2015-09-11T11:16:20Z
dc.date.issued 2012-07-05 tr_TR
dc.description Tez (Yüksek Lisans) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2012 tr_TR
dc.description Thesis (M.Sc.) -- İstanbul Technical University, Institute of Science and Technology, 2012 en_US
dc.description.abstract Deneysel çalışmalar kapsamında Al2O3-YSZ-CeO2 kompozitleri SPS tekniği ile üretilmiştir. İlk aşamada hacimce farklı oranlarda (%5, 15 ve 25) YSZ içeriği ile hazırlanan Al2O3 – YSZ kompozitlerine ikinci aşamada ağırlıkça %3 ve %5 CeO2 katılmıştır. CeO2 ilavesinin Al2O3-YSZ-CeO2 kompozitlerinin yapısında oluşturduğu mikroyapısal ve mekanik etkiler incelenerek karakterizasyonu yapılmıştır. Saf Al2O3’e YSZ ilavesi, oluşan kompozitlerin Vickers mikrosertlik ve kırılma tokluğu değerini arttırmıştır. Artan sertlik ve kırılma tokluk değerinin YSZ’nin göstermiş olduğu dönüşüm toklaşması özelliğinden kaynaklandığı düşünülmektedir. Al2O3-YSZ kompozitlerinin mekanik özelliklerine CeO2’nin etkisi incelendiğinde, CeO2 oranı %3’ten %5’e çıkarıldığında sertlikte azalma gözlenmiştir. Benzer şekilde CeO2 miktarı arttıkça, kırılma tokluğunda azalma gözlenmiştir. Mikroyapı incelemeleri sonucunda kırılma tokluğunda meydana gelen düşüşün seryum alüminat tanelerinde sapmaya uğramadan geçen çatlak ilerleyişinden kaynaklandığı düşünülmektedir. Hücre kültürü testlerine göre osteoblast hücreleri Al2O3-YSZ ve Al2O3-YSZ-CeO2 numuneleri bulunan kültür ortamında büyümeye devam etmiş, olumlu veya olumsuz herhangi bir etkileşime girmediği görülmüştür. tr_TR
dc.description.abstract This study aims to show the effects of 3 and 5 mass% ceria (CeO2) additions on the densification, microstructures, mechanical and biocompatibility properties of 3 mol% yttria-stabilised zirconia (YSZ) toughened alumina. Al2O3 based composites were prepared by spark plasma sintering (SPS) at 1350-1400˚C for 300s under a pressure of 40 MPa. Fully dense composites were obtained. It was observed that the addition of 5 vol% zirconia inhibites the grain growth of alumina and containing 3 and 5 mass% ceria composites leads to the formation of elongated CeAl11O18 grains. The samples were subjected to mechanical tests like Vickers hardness and fracture toughness. Hardness of Al2O3 composites containing 3 mol% yttria-stabilized zirconia had higher value when compared to monolithic Al2O3 and Al3O3-YSZ composites with CeO2. Hardness of Al2O3-YSZ composites decreased from 20.0 GPa to 19.0 GPa when the content of YSZ increased from 15 to 25 vol%. Moreover, fracture toughness of Al2O3-YSZ composites increased from 3.0 MPa•m1/2 to 4.1 MPa•m1/2 with the increasing amount of YSZ from 5 to 25 vol%. Because of the fact that the expansion of the inclusions when the zirconia activate the tetragonal to monoclinic phase transformation, having highest rate of YSZ into Al2O3–YSZ composites with or without CeO2 provides highest fracture toughness values. Cell viability and alkaline phosphates activity in the presence of samples were studied and cell viability/proliferation was not prevented by the presence of samples. The cell culture test (cell viability and alkaline phosphatese tests) showed that Al2O3-YSZ ceramics containing %15 YSZ with 3 and 5 mass% CeO2 showed almost same cell viability and alkaline phosphates activity when compared to control and also better than without CeO2. en_US
dc.description.degree Yüksek Lisans tr_TR
dc.description.degree M.Sc. en_US
dc.identifier.uri http://hdl.handle.net/11527/9227
dc.publisher Fen Bilimleri Enstitüsü tr_TR
dc.publisher Institute of Science and Technology en_US
dc.rights İTÜ tezleri telif hakkı ile korunmaktadır. Bunlar, bu kaynak üzerinden herhangi bir amaçla görüntülenebilir, ancak yazılı izin alınmadan herhangi bir biçimde yeniden oluşturulması veya dağıtılması yasaklanmıştır. tr_TR
dc.rights İTÜ theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. en_US
dc.subject alümina tr_TR
dc.subject itriya ile stabilize edilmiş zirkonya tr_TR
dc.subject seryum dioksit tr_TR
dc.subject spark plazma sinterleme tr_TR
dc.subject yttria-stabilized zirconia en_US
dc.subject cerium dioxide en_US
dc.subject spark plasma sintering en_US
dc.title Al2o3 – Zro2 – Ceo2 Kompozitlerinin Spark Plazma Sinterleme (sps)yöntemi İle Üretimi Ve Karakterizasyonu tr_TR
dc.title.alternative Production And Characterization Of Al2o3 – Zro2 – Ceo2 Composites By Spark Plasma Sintering (sps) en_US
dc.type Thesis en_US
dc.type Tez tr_TR
Dosyalar
Orijinal seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.placeholder
Ad:
12754.pdf
Boyut:
2.21 MB
Format:
Adobe Portable Document Format
Açıklama
Lisanslı seri
Şimdi gösteriliyor 1 - 1 / 1
thumbnail.default.placeholder
Ad:
license.txt
Boyut:
3.14 KB
Format:
Plain Text
Açıklama