Title: Beypazarı Ve Kazan Trona Cevherlerinin Flotasyon Ve Manyetik Ayırma Yöntemleriyle Zenginleştirilmesi
Other Titles: Processing Of Beypazari And Kazan Trona By Flotation And Magnetic Separation Methods
Authors: Çelik, Mehmet Sabri
Matazimov, Daniyar
Cevher Kömür Hazırlama ve Değerlendirme
Coal and Mineral Processing
Keywords: Trona
Sodyum Seskikarbonat
Sodyum Karbonat
Sodyum Bikarbonat
Flotasyon
Manyetik Ayırma
Trona
Sodium Sesquicarbonate
Sodium Carbonate
Sodium Bicarbonate
Magnetic Seperation
Publisher: Fen Bilimleri Enstitüsü
Institute of Science and Technology
Abstract: u çalışmada, Beypazarı ve Kazan trona cevherlerinin flotasyon yöntemiyle trona içeriğinin yükseltilmesi çalışmaları yapılarak, yüksek trona içeriğine sahip Beypazarı trona cevherinin % 65 PKO, 2.50 kg/ton DAH miktarı, 6.25 kg/ton gazyağı miktarı ve 90 saniye flotasyon süresinde optimum verim elde edilmiştir. Düşük trona içeren Kazan trona cevherinin iki farklı boyut grubu (-0,5+0,212 mm ve -0,212+0,038 mm) için DAH miktarına bağlı olarak yapılan flotasyon çalışmalarda, optimim DAH mikarının -0,5+0,212 mm boyut grubu için 2,5 kg/ton, -0,212+0,038 mm boyut grubu için de 5 kg/ton olduğu elde edilmiştir. Beypazarı ve Kazan trona cevherlerinin manyetik ayırma ile ön zenginleştirmeye de tabi tutulmuştur. Manyetik ayırma sonucu -1+0,5 mm ve -0,5+0,212 mm tane boyutlarında Beypazarı trona cevherlerinin trona içeriği % 97,20’ye yükseltilmiştir. Kazan trona cevherinin manyetik ayırma sonucu -0,5+0,212 mm tane boyutu için kısmen zenginleşme olmuştur, -0,212+0,038 mm tane boyutu için ise zenginleşme görülmemiştir. Özetle, elde edilen flotasyon sonuçları özellikle düşük trona içeren Kazan tronası için ümit vaat etmektedir. İyi bir optimizasyon ile manyetik ayırma işlemi de flotasyon öncesi bir ön zenginleştirme işlemi olarak dikkate alınması da öngörülmüştür.
This study aims to remove as much impurity as possible from ‘Beypazarı’ and ‘Kazan’ trona ores by flotation and magnetic separation methods. The impurities in the Beypazarı trona ore sample of –1+0,5 mm in size did not float when the conditioning of trona with the emulsion composed of DAH as collector and kerosene as emulsifier was prepared in a separate conditioning tank. It was found that the addition of some brine during the condition made the impurities float. Because of this observation brine was added to the conditioning tank throughout the experiments. Experiments made as a functions of pulp density, amount of DAH collector and kerosene, and flotation time. In summary, the flotation process of trona under the conditions of 65 % by weight, 2.5 kg/t DAH collector, 6.25 kg/ton kerosene and 90 second flotation time gave the best results and the content of trona increased from % 95,92 to % 99,27 with a recovery of 73,08 %. Because the trona content of Kazan ore (55 %) is less than Beypazarı trona ore the amount of collector has been studied. The two size groups (-0,5+0,212 mm and 0,212+0,038 mm) of ore were subjected to flotation with the aim of optimizing the amount of DAH and kerosene; 2,5 kg/ton and 5 kg/ton, respectively were found to be the optimum. While the -0,5+0,212 mm trona ore was upgraded to % 91,75 % with a yield of 82,27 %, –0,212+0,038 mm trona was enriched to 92,13 % with a yield of 61,88 %. Magnetic separation method was applied to both Beypazarı and Kazan trona ores. Beypazarı trona prepared in –0,5+0,212 mm and –0,212+0,038 mm size fractions. The non-magnetic product was upgraded to 97,20 % with a yield of 71,08 % and 64,43 %, respectively. Magnetic separation of Kazan trona ore exhibited different results. –0,5+0,212 mm trona ore sample was not much successful despite excellent visual colour separation. -05+0.038 mm size fraction produced better results but not sufficient. It was found that although colour separation was unusually successful, trona is only partly liberated. Therefore, middlings require further size reduction to enable better grade and recoveries.
Description: Tez (Yüksek Lisans) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2005
Thesis (M.Sc.) -- İstanbul Technical University, Institute of Science and Technology, 2005
URI: http://hdl.handle.net/11527/10522
Appears in Collections:Cevher Hazırlama Mühendisliği Lisansüstü Programı - Yüksek Lisans

Files in This Item:
File Description SizeFormat 
8162.pdf8.04 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.