Grafen Takviyeli Biyokompozitlerin Mekanik Ve Termal Özelliklerinin İncelenmesi

Abstract

Chitosan polymer was reinforced with graphene nanoparticles in this study. Polymeric composites were prepared by the solution casting technique using graphene at different weight ratios. Tensile tests were carried out to determine tensile strength and Young’s modulus of the composites. The effect of graphene on thermal conductivity of chitosan was also determined. The tensile strength and Young’s modulus of chitosan increased by approximately 72 % and 170 %, respectively when 3 wt.% of graphene was added into chitosan. The thermal conductivity values of these composites were obtained to be higher in comparison with that of chitosan.Bu çalışmada kitosan biyopolimeri grafen nanopartikülleri ile takviye edilmiştir. Polimerik kompozitler ağırlıkça farklı oranlarda grafen kullanılarak çözelti döküm tekniği ile hazırlanmıştır. Çekme testleri kompozitlerin çekme dayanımı ve Young modülünü belirlemek için gerçekleştirilmiştir. Ayrıca kitosanın termal iletkenliğine grafenin etkisi tespit edilmiştir. % 2 grafen kitosan içerine katıldığında, kitosanın çekme dayanımı ve Young Modülü sırasıyla % 72 ve % 170 artmıştır. Kompozitlerin termal iletkenliği kitosan ile kıyaslandığında çok daha yüksek olduğu tespit edilmiştir.Conference Paper -- Theoretical and Applied Mechanical Turkish National Committee, 2015Konferans Bildirisi -- Teorik ve Uygulamalı Mekanik Türk Milli Komitesi, 2015