The effect of dispersion technique, silver particle loading, and reduction method on the properties of polyacrylonitrile–silver composite nanofiber

Abstract

The effect of dispersion technique, reduction method, and the amount of silver nanoparticles on the properties of composite polyacrylonitrile nanofiber containing silver nanoparticles is analyzed using differential scanning calorimetry, scanning electron microscopy, electrical conductivity, tensile testing, X-ray diffraction, and antimicrobial efficiency measurements. Composite nanofibers reduced by hydrazine hydroxide result in smaller diameter, higher electrical conductivity, higher breaking strength, higher cyclization enthalpy than the samples reduced by xenon arc method. Reduction process results in smaller diameter and higher breaking strength than those of non-reduced nanofiber web containing AgNO3 nanoparticles. Dispersion by ultrasonic homogenizer/bath provides higher breaking strength, electrical conductivity than the samples dispersed by only magnetic stirrer. An increase of silver nanoparticle generally results in an increase of enthalpy, a decrease of both cyclization temperatures and crystallinity. While 1 wt% AgNO3 loading is suitable for high breaking strength, 3 wt% AgNO3 loading is suitable for both high electrical conductivity and antimicrobial properties. Insulator polyacrylonitrile polymer becomes a semiconducting material.