Structural and spectroscopic properties of Nd 3+ :Y 2 Si 2 O 7 phosphors

Abstract

Abstract Phosphors of α -Y 2 Si 2 O 7 doped with Nd 3+ ions were prepared using the sol–gel technique. Nano-sized crystalline phosphor powders were obtained by annealing the dried gels at 960 °C. The crystallization properties of the phosphor powders were determined from their XRD patterns. The α -Y 2 Si 2 O 7 phase was the only phase observed in all compositions. As the amount of amorphous SiO 2 in the composition was increased, the crystalline sizes and the widths of the size distribution curves were found to decrease from 17.8 nm to 10.6 nm and from 15.6 nm to 12.2 nm, respectively. The spectroscopic properties of the powders were studied by measuring the luminescence and the decay patterns of the 4 F 3/2 → 4 I 9/2 and 4 F 3/2 → 4 I 11/2 transitions between 50 K and 310 K. No appreciable effect of the crystallite sizes on the average lifetime of the 4 F 3/2 level was observed at temperatures below 100 K. The effect of temperature, however, becomes relevant above 100 K as the size of α -Y 2 Si 2 O 7 nano-crystal becomes smaller.