Photoinduced Polymerization of Thiophene Using Iodonium Salt

Abstract

AbstractSummary: Thiophene was polymerized by means of UV irradiation using diphenyliodonium hexafluorophosphate as a photoinitiator. An initiation mechanism involving electron transfer from photochemically generated onium radical cations to thiophene was proposed. N‐Ethoxy‐2‐methylpyridinium hexafluorophosphate and triphenylsulfonium hexafluorophosphate were also found to be effective in facilitating the polymerization of thiophene. Polymerization is accompanied with the film formation on the surface of the reaction tube. The photochemically obtained polymers were characterized by FT‐IR, DSC, and SEM analyses and compared with those obtained by oxidative and electrochemical means. Electrical conductivities of the samples were measured by four‐probe technique.Photograph of the polymerization mixture containing thiophene and iodonium salt in CH2Cl2 before (a), after 5 min of irradiation (b), and dried film (c).magnified imagePhotograph of the polymerization mixture containing thiophene and iodonium salt in CH2Cl2 before (a), after 5 min of irradiation (b), and dried film (c).