Concentration effect of Er 3+ ions on structural and spectroscopic properties of CdNb 2 O 6 phosphors

Abstract

Excitation and emission spectra of a visible room-temperature Er{sup 3+} ions luminescence from powders. - Highlights: • This is the first report on spectroscopic properties of CdNb{sub 2}O{sub 6}:Er{sup 3+}. • The crystalline sizes are affected as the concentration of Er{sup 3+} ions increased. • Quenching of the luminescence was observed to be above 1.0 mol% Er{sup 3+}. - Abstract: This study is focused on the synthesis and characterization of CdNb{sub 2}O{sub 6} compounds doped with of Er{sup 3+} ions. Powders were synthesized by using the molten salt method and annealed at 900 °C for 4 h. The synthesized particles were structurally characterized by using X-ray diffraction, scanning electron microscopy. A single phase of the CdNb{sub 2}O{sub 6} was determined and the size of the particles was found to be affected by the presence and the concentration of Er{sup 3+} ions. Luminescence properties of each sample were investigated by measuring accurately the emission and excitation spectra at room temperature in the wavelength range of 200–1700 nm by exciting the Er{sup 3+} ions at 379 nm and 805 nm. Quenching of the luminescence in both visible and near infrared spectral regions was observed to be above 1.0 mol% Er{sup 3+} concentration.