Production of CrB2 Powder Via Self Propagating High Temperature Synthesis

Abstract

ZrB2 and TiB2 are one of the most significant metal borides. They are being used in various industrial areas from space technology to nuclear industry owing to their physical properties such as high melting point, high thermal/electrical conductivity and low density. Present study was conducted in two main stages: Self-propagating high-temperature synthesis (SHS) reactions and leaching. ZrO2, TiO2, B2O3 were used as starting material and Mg used as a reductant to produce ZrB2-TiB2 powders via SHS. Therefore, it was aimed to determine production parameters, leaching conditions and comprehensive examination of final product features. The samples were characterized by using chemical analysis (AAS), XRD, XRF and SEM/EDS techniques.