Title: Iı-vı Grubu Yarıiletken Nano Yapılı İnce Filmlerin Sol-jel Yöntemi İle Üretimi
Other Titles: The Production Of Nanostructured Thin Films Using Ii-vi Group Semiconductors By Sol-gel Method
Authors: Tepehan, Fatma Z.
Koç, Kenan
421093
Fizik Mühendisliği
Physics Engineering
Keywords: CdS kuantum noktalar
ZnS kuantum noktalar
Sol-jel yöntemi
CdS quantum dots
ZnS quantum dots
Sol-gel method
Issue Date: 16-Jan-2012
Publisher: Fen Bilimleri Enstitüsü
Institute of Science and Technology
Abstract: Bu çalışmada kolloidal, toz ve ince film formundaki 3-mercaptopropyltrimethoxysilane (MPS) kuşatımlı CdS ve ZnS kuantum noktalar sol-jel yöntemi ile üretilmiştir. Kolloidal ve toz formunda üretilen kuantum noktaların boyutları 2.5-3 nm arasında bulunmuştur. Kolloidal nanoparçacıklar başka bir matris içine katılmadan kendiliğinden monte olarak doğrudan cam taşıyıcı üzerine döndürerek kaplama yöntemi ile kaplanmıştır. Üretilen filmlere ısıl işlem uygulanmış ve Oswald olgunlaşması nedeni ile ısıl işlem sıcaklığı ve süresi artığında kuantum noktaların ortalama boyutlarının artığı gözlenmiştir. Kuantum noktaların ısıl işlemle büyüme süreci LSW teorisine göre incelenmiştir. Bu çalışmada üretilen filmlerin optik ve yapısal özellikleri de incelenmiştir. Bu incelemeler sonucunda filmlerin kırma indisleri, söndürme katsayıları, dielektrik sabitleri ve kalınlıkları bulunmuştur.
In this study, colloidal, powdered and thin film forms of 3-mercaptopropyltrimethoxysilane (MPS)-capped CdS and ZnS quantum dots have been produced by sol-gel method. The sizes of quantum dots produced in colloidal and powder forms were found in between 2.5 and 3 nm. Colloidal nanoparticles were self-assembled directly on a glass substrate using spin coating method without introducing any matrix. Thermal treatment was applied to the produced films and it was observed that as the treatment temperature and time increased, the average diameter of quantum dots increased due to Ostwald ripening. The thermal process used to grow the size of quantum dots was examined according to LSW theory. In this study, also the optical and structural characteristics of the produced films were investigated. As a result of these investigations, the refractive index, extinction coefficients, dielectric constants, and the thicknesses of the films were determined.
Description: Tez (Doktora) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2011
Thesis (PhD) -- İstanbul Technical University, Institute of Science and Technology, 2011
URI: http://hdl.handle.net/11527/7191
Appears in Collections:Fizik Mühendisliği Lisansüstü Programı - Doktora

Files in This Item:
File Description SizeFormat 
12184.pdf3.01 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.